D3518/D3518M Standard Test Method for In-Plane Shear Response of Polymer Matrix Composite Materials by Tensile Test of a #xb1;45#xb0; Laminate has been revised to D3518/D3518M-18

» Código: ASTM D3518 / D3518M - 18

» Comité: Subcommittee: D30.04

» Más información

Solicitar Norma

Significance and Use

5.1 This test method is designed to produce in-plane shear property data for material specifications, research and development, quality assurance, and structural design and analysis. Factors that influence the shear response and should therefore be reported include the following: material, methods of material preparation and lay-up, specimen stacking sequence and overall thickness, specimen preparation, specimen conditioning, environment of testing, specimen alignment and gripping, speed of testing, time at temperature, void content, and volume percent reinforcement. Properties that may be derived from this test method include the following:

5.1.1 In-plane shear stress versus shear strain response,

5.1.2 In-plane shear chord modulus of elasticity,

5.1.3 Offset shear properties,

5.1.4 Maximum in-plane shear stress for a ±45° laminate, and

5.1.5 Maximum in-plane engineering shear strain for a ±45° laminate.

1. Scope

1.1 This test method determines the in-plane shear response of polymer matrix composite materials reinforced by high-modulus fibers. The composite material form is limited to a continuous-fiber-reinforced composite ±45° laminate capable of being tension tested in the laminate x direction.

1.2 The values stated in either SI units or inch-pound units are to be regarded separately as standard. The values stated in each system are not exact equivalents; therefore, each system must be used independently of the other. Combining values from the two systems may result in nonconformance with the standard.

1.2.1 Within the text, the inch-pound units are shown in brackets.

1.3 This standard does not purport to address all of the safety concerns, if any, associated with its use. It is the responsibility of the user of this standard to establish appropriate safety, health, and environmental practices and determine the applicability of regulatory limitations prior to use.

1.4 This international standard was developed in accordance with internationally recognized principles on standardization established in the Decision on Principles for the Development of International Standards, Guides and Recommendations issued by the World Trade Organization Technical Barriers to Trade (TBT) Committee.


2. Referenced Documents (purchase separately) The documents listed below are referenced within the subject standard but are not provided as part of the standard.

ASTM Standards

D883 Terminology Relating to Plastics

D3039/D3039M Test Method for Tensile Properties of Polymer Matrix Composite Materials

D3878 Terminology for Composite Materials

D5229/D5229M Test Method for Moisture Absorption Properties and Equilibrium Conditioning of Polymer Matrix Composite Materials

E6 Terminology Relating to Methods of Mechanical Testing

E111 Test Method for Youngs Modulus, Tangent Modulus, and Chord Modulus

E177 Practice for Use of the Terms Precision and Bias in ASTM Test Methods

E456 Terminology Relating to Quality and Statistics

RECOMENDAR
Su nombre:
Correo-e destinatario:
*Para varios destinatarios, utilice la coma como separador
Comentarios:
Delicious Menéame
Yahoo
Buzz!

Financiado por: